Talk:Amorphous solid
![]() | This ![]() It is of interest to the following WikiProjects: | ||||||||||||||||||||||||||||||
|
![]() | This article is substantially duplicated by a piece in an external publication. Since the external publication copied Wikipedia rather than the reverse, please do not flag this article as a copyright violation of the following source:
|
![]() | This article links to one or more target anchors that no longer exist.
Please help fix the broken anchors. You can remove this template after fixing the problems. | Reporting errors |
Flowing
[edit]Should there be a mention of the urban legend that glass flows?
"Do Cathedral Glasses Flow?", Am. J. Phys. v66, pp 392-396, May, 1998
http://www.glassnotes.com/WindowPanes.html
http://www.phschool.com/science/science_news/articles/property_glass.html
http://www.maths.adelaide.edu.au/people/ystokes/windows.html
- There is one in the glass page, but I'll make mention of it in this article.--Polyparadigm 02:00, 16 Feb 2005 (UTC)
- It's not an urban legend. Glass actually does flow, or rather, at least some types do; I've personally witnessed the effects. The house I grew up in was completed in 1932, and by the time I left there in 1999, the two remaining panes in the entire house that were original were easy to identify, because they were nearly 4 times as thick at their bottom edge than their tops, with a smooth taper from top to bottom, and some slight rippling, very similar in appearance to super-high-speed photos of flowing water. On the other hand, on vacation, I once visited the home of one of the USA founding fathers (I think it was Jefferson), and noted that some panes there, supposedly original, and thus far older than 1932, showed no macroscopically perceptible signs of flowing; I have speculated that the glass from that site was probably so-called "lead crystal", both due to the context in which it was made, and because it exhibited that material's distictive appearance. The same property of lead crystal that leads to its distictive ring ("Since the potash ions are bound more tightly in a lead-silica matrix than in a soda-lime glass", quoted from the wikipedia "lead glass" article), would also be reasonably expected to cause it to flow significantly more slowly. 67.162.34.172 (talk) 02:03, 19 December 2009 (UTC)
- Glass is a solid. It is not a fluid. It does not flow, not even on geological timescales. There is absolutely no scientific evidence whatsoever that will back up your claims. The myth is the result of old methods of forming glass where one end of a pane was often thicker than the other. It makes sense to install the window pane with the thicker end at the bottom. Indeed there are cases where window panes were installed with the thicker end at the top! Polyamorph (talk) 10:24, 19 December 2009 (UTC)
- From our glass article (which is fully referenced):
“ | In glass factories, molten glass was poured onto a large cooling table and allowed to spread. The resulting glass is thicker at the location of the pour, located at the center of the large sheet. These sheets were cut into smaller window panes with nonuniform thickness. Modern glass intended for windows is produced as float glass and is very uniform in thickness.
Several other points exemplify the misconception of the "cathedral glass" theory:
|
” |
Polyamorph (talk) 10:33, 19 December 2009 (UTC)
It is not just about thicker ends of the pane mounted at the bottom, the panes in the house I grew up in were perceptibly molded to the contours of the wood they were mounted in. Obsidian blades, cathedral panes, and telescope lenses are all made of specialized types of glass, and none of them are even particularly close to being the same type as was commonly used in residential windows in the 1920s. Siting 3 examples of cases where something didn't happen proves only that it doesn't happen in those particular cases, not that it can never happen in any case. I don't doubt that there are types of glass that either flow so slowly as to require geological timeframes to be significant, or even that don't flow at all at moderate temperatures, but that's not all glass. 67.162.34.172 (talk) 04:38, 16 May 2010 (UTC)
- You are mistaken and I am still waiting for someone to provide a citation that proves that any form of glass flows. This is not the first of this kind of discussion and not once has anyone been able to cite a verifiable and accurate source that proves the claim that glass flows. That is because it is scientifically incorrect. Glass is a solid and is hence just as rigid as any crystalline material. Polyamorph (talk) 08:28, 16 May 2010 (UTC)
Ice
[edit]ice is a hydrogen bonded molecular crystalline solid Ice is an amorphous solid? Acegikmo1 14:41, 17 Sep 2004 (UTC)
- I've removed it, along with other substances that I'm fairly sure aren't amorphous solids, from the article. Acegikmo1 00:13, 17 Oct 2004 (UTC)
- Ice does have several amorphous phases Polyamorph (talk) 19:20, 15 December 2007 (UTC)
- See Amorphous ice. As with many crystalline materials which have distinct polymorphic structures, they may indeed also have several distinct polyamorphic structures. Polyamorph (talk) 08:55, 21 February 2009 (UTC)
Glass: substance or another word for amorphous solid
[edit]This article suggests that "amorphous solid" and "glass" (in the broad sense) differ in that all glasses are amorphous solids but not all amorphous solids are glasses:
"The terms "glass" and "glassy solid" are sometimes used synonymously with amorphous solid; however, these terms refer specifically to amorphous materials that undergo a glass transition."
Somewhere, either here or at the article on glass transitions (maybe both places) there really needs to be an example of an amorphous solid that is not a glass. If we can't come up with one, the two articles should be merged.
From earlier:
The article is a little confusing because it contains several inconsistent definitions of the word glass. In the first half of the article it refers to a liquid that is cooled below the [glass transition temperature]], but in the second half it refers to common glass
Supercool vs Glass transition
[edit]Some liquids have a glass transition temperature that is higher than the melting point. This means that you can create a glass without supercooling the liquids. Therefore the following sentence is wrong
Tg cannot be greater than the melting temperature. Above the melting temperature, the substance is an isotropic liquid with a viscosity well below that of a glass. ---Dan Miller —Preceding unsigned comment added by 67.188.147.13 (talk) 22:08, 2 December 2007 (UTC)
"Glass is often referred to as a 'super-cooled' liquid.". glass is called a super cooled liquid because of its ability to flow in heating.It is also called a pseudo-solid However it is correct to write that "Some substances can only be cooled below the glass transition temperature if they are supercooled."
One line says that glass is an amorphous ceramic. Is this correct? I have never heard this before and can find no corroboration in the Glass article. Garbagemania (talk) 02:43, 30 January 2009 (UTC)
- Sometimes glasses are referred to as an amorphous ceramic but in this case I would tend to agree with you that this is just confusing. This entire article needs re-writing anyway, it seems to focus on glassy materials when these are extensively dealt with in the glass article. Although glasses are certainly amorphous solids and deserve a mention, I think this article should be dealing with materials manufactured using, for example, vapour deposition, splat quenching or sol-gel methods, to name but a few. Polyamorph (talk) 09:33, 30 January 2009 (UTC)
The definition
[edit]An amorphous solid is a solid in which there is no long-range order of the positions of the atoms. (Solids in which there is long-range atomic order are called crystalline solids.)
Should we write "an amorphous solid is a solid in which the position of the atoms is in short-range order without long-range order"? Roscoe x 13:31, 16 Nov 2004 (UTC)
amorphous solids are solids having short range order.
- No, the key concept here is the fact that amorphous solids lack long range translational periodicity, they will have a high degree of short range order by virtue of atomic bonding characteristics, and may even exhibit ordering on intermediate length scales. I agree that the article is poorly written though and should be re-worded to make the concept clearer. Polyamorph (talk) 09:28, 30 January 2009 (UTC)
- We can also add the fact that an amorphous solid is pretty much the intermediate stage between a crystalline solid and a liquid. Majopius (talk) 01:03, 23 April 2009 (UTC)
- Except that it isn't an intermediate stage, cooling a liquid below its melting temperature will typically lead to a crystalline solid there is no intermediate amorphous stage. The structure of an amorphous solid is, however, analagous to that of a liquid which is what I think you were referring to. Polyamorph (talk) 08:58, 23 April 2009 (UTC)
Eutectic system
[edit]You should be linking here to the explanation on the eutectic reaction. Metallic glasses are most easily formed when working with compositions as close as possible to deep eutectic systems. —Preceding unsigned comment added by 178.198.133.52 (talk) 21:22, 12 October 2010 (UTC)
Caption needs more info
[edit]![](http://upload.wikimedia.org/wikipedia/commons/thumb/1/16/Order_and_Connectivity.jpg/220px-Order_and_Connectivity.jpg)
This graphic is good, but the caption needs to say which cell(s) are considered amorphous. Loraof (talk) 16:39, 6 February 2017 (UTC)
The combination of caption and graphic are lacking and do not help someone unless they are already familiar with the concepts. Furthermore, there isn't much related discussion in the text about liquid crystals, or crystals vs. metal for that matter. The source does not have more information. This should be reconsidered in the text, revised, or remove the graphic entirely. 99.224.2.208 (talk) 03:09, 15 January 2019 (UTC)
Move discussion in progress
[edit]There is a move discussion in progress on Talk:Amorphous (album) which affects this page. Please participate on that page and not in this talk page section. Thank you. —RMCD bot 04:06, 1 March 2021 (UTC)
- B-Class vital articles
- Wikipedia level-4 vital articles
- Wikipedia vital articles in Physical sciences
- B-Class level-4 vital articles
- Wikipedia level-4 vital articles in Physical sciences
- B-Class vital articles in Physical sciences
- B-Class physics articles
- High-importance physics articles
- B-Class physics articles of High-importance
- B-Class glass articles
- Top-importance glass articles
- B-Class glass articles of Top-importance
- WikiProject Glass articles
- B-Class Materials articles
- High-importance Materials articles
- WikiProject Materials articles